Structures by: Bobylev A. P.
Total: 8
K3 Eu (P O4)2
EuK3O8P2
Zhurnal Neorganicheskoi Khimii (2001) 46, 805-813
a=9.455Å b=5.6229Å c=7.4185Å
α=90° β=90.867° γ=90°
K3 Eu (V O4)2
EuK3O8V2
Zhurnal Neorganicheskoi Khimii (2001) 46, 805-813
a=9.8391Å b=5.91Å c=7.5203Å
α=90° β=90.855° γ=90°
Na Er F (P O4)
ErFNaO4P
Zhurnal Neorganicheskoi Khimii (2001) 46, 1629-1634
a=8.9214Å b=6.9194Å c=6.4517Å
α=90° β=106.166° γ=90°
K In (H P O4)2
H2InKO8P2
Zhurnal Neorganicheskoi Khimii (2002) 47, 1930-1946
a=9.6232Å b=8.2573Å c=9.4571Å
α=90° β=115.72° γ=90°
(N H4) In (H P O4)2
H6InNO8P2
Zhurnal Neorganicheskoi Khimii (2002) 47, 1930-1946
a=9.6651Å b=8.2763Å c=9.5964Å
α=90° β=116.15° γ=90°
Rb In (H P O4)2
H2InO8P2Rb
Zhurnal Neorganicheskoi Khimii (2002) 47, 1930-1946
a=9.705Å b=8.367Å c=9.528Å
α=90° β=116.6° γ=90°
Mercury barium calcium copper oxide (0.69/2/2/3/8.6)
Ba2Ca2Cu3Hg0.692O8.6
Physica C (Amsterdam) (152,1988-) (1995) 243, 222-232
a=3.86521(7)Å b=3.86521(7)Å c=15.6486(4)Å
α=90° β=90° γ=90°
Na3 In (P O4)2
InNa3O8P2
Journal of Solid State Chemistry (2000) 149, 99-106
a=8.6335Å b=5.455Å c=7.0482Å
α=90° β=90.295° γ=90°